Grade 316 (L)

UNS S31600 : ASTM A182 (VO1.01), A276 (VO1.03), A479 (VO1.03), BS EN 10088

Chemical composition

L grade limits C to 0.03 max.
C Si Mn P S Cr Ni Mo N Fe
Min 16.00 10.00 2.00 0.00
Max 0.08 1.00 2.00 0.045 0.030 18.00 14.00 3.00 0.10 0.00

Mechanical properties

Condition: Solution Annealed

NACE MR0175 limits the supply hardness to 22 HRC max.
U.T.S 75 KSI Min (515 N/mm2)
0.2% Proof Stress 30 KSI Min (205 N/mm2)
Elongation 30 %
Red of Area 50 %
CVN Impacts @ -75°C (-100°F) 135 Joules (100 ft-lbf)
Size range: 1/8”∅ - 20”∅

General scope

316L is an austenitic stainless steel from the 300 series 18/8 family. 316L is similar in composition and strength to 304L stainless steel with the main difference being the addition of 2.0% Molybdenum. The addition of Molybdenum gives the grade improved corrosion resistance.

316l is normally supplied Solution Annealed/Treated although it can be supplied cold worked with higher strength properties. The "L" grade has a reduced carbon level to improve corrosion resistance after welding, and is generally more commonly available.

NACE MR0175 - 2003 "general use" approval now limits the maximum environmental temperature to 140°F (60°C).