Grade F6NM
UNS S41500 : ASTM A182 (VO1.01)
Chemical composition
|
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Mo |
Fe |
| Min |
• |
• |
0.50 |
• |
• |
11.50 |
3.5 |
0.50 |
0.0000000000 |
| Max |
0.05 |
0.60 |
1.00 |
0.030 |
0.030 |
14.00 |
5.5 |
1.00 |
0.0000000000 |
Mechanical properties
Condition: Hardened and Double Tempered
NACE MR0175 limits the supply hardness to 23 HRC max.
| U.T.S. |
95 KSI min |
(655 N/mm²) |
| 0.2% Proof Stress |
75 KSI min |
(517 N/mm²) |
| Elongation |
18% |
|
| Red of Area |
35% |
|
| CVN Impacts @ -60°C (-75°F) |
40 Joules |
(30ft-lbf) |
General scope
ASTM A182 is a martensitic stainless steel. The additions of Nickel and Molybdenum, which gives it excellent sub zero notch ductility, superior to other standard 13 Cr, 410 and 420 Mod martensitic stainless steels.
UNS S41500 steel is air hardening, with little danger of thick sections cracking during heat treatment.
In addition to limiting the maximum hardness allowed to 23 HRC max, NACE MR0175 imposes heat treatment temperature restrictions.
The weldability and corrosion resistance of ASTM A182 are also excellent, being extensively used in the manufacture of Valve Bodies, Flanges, Seats, Gates, Tubulars, etc.
ASTM A182 specifies a minimum 0.2 PS value of 95 KSI. This NACE approved grade is limited to 75 KSI because of the hardness restriction.